Effect of Al on bulk amorphization and magnetic properties of FeSnPSiB alloys

[[abstract]]Structure and magnetic properties of melt-spun multi-component Fe78-xAlxSn2P12 Si4B4 (x = 0, 3, 4, 5 at%) amorphous ribbons and copper-mold-cast rods were investigated. The improvement of thermal stability was recognized with the replacement of Fe by 3similar to5 at% Al in these Sn-containing alloys. The super-cooled liquid region (DeltaT(x)), defined by (T-x - T-g) where T-x is the crystallization temperature and T-g the glass transition temperature, increases from 46.5 K as x = 3 to the maximum value 50.2 K as x = 4. With increasing Al content, magnetic properties of annealed Fe78-xAlxSn2P12Si4B4 (x = 3similar to5 at%) amorphous ribbons are: saturation magnetization decreases from 1.22 to 1.18 T; coercive force decreases from 3.3 to 2.2 A/m, maximum permeability increases from 137000 to 208000, Curie temperature lowers from 591.1 K to 578.3 K; the electrical resistivity increases from 175 to 188 muOmega-cm; and core loss is about 0.14W/kg (50Hz, 1.1 T external magnetic field). Bulk amorphous rods with 1 mm diameter were successfully demonstrated for the composition Fe(74)Al(4)Sn(2)Pl(2)Si(4)B(4) by a copper mold casting method. Due to the combination of good glass forming ability and superior soft magnetic properties, these alloys will find potential applications in industries.[[fileno]]2020336010100[[department]]材料