The effect of Ag electrode processing on (Nb,Ba) doped TiO2 ceramics

[[abstract]]Since the characteristics of the electrode made from Ag paste greatly affect the dielectric properties of (Nb,Ba) doped TiO2 ceramics, the processing condition, i.e. baking temperature, was investigated. Low melting glass binder contained in Ag paste reacted with TiO2 ceramics to form an interface layer between Ag electrode and TiO2 ceramics during baking. The interface layer was identified as Bi2Ti2O7 by X-ray diffraction (XRD), and the thickness of the Bi2Ti2O7 layer was estimated from line profiles of EPMA and dielectric properties. The interface layers were found to increase with baking temperature. Increased baking temperature lowered the relative dielectric constant and dielectric dissipation factor of TiO2 ceramics, while it raised the resistivity. Controlling the baking condition of the Ag paste electrode on TiO2 ceramics resulted in reasonably good dielectric properties and excellent temperature stability[[fileno]]2020301010031[[department]]材料科學工程學