Electrochemical characterization of activated carbon-ruthenium oxide nanoparticles composites for supercapacitors

[[abstract]]©2004 Elsevier - The high specific capacitance of ruthenium oxide (denoted as RuOx ) nanoparticles prepared by a modified sol-gel method with annealing in air for supercapacitors was demonstrated in this work. The specific capacitance of activated carbon (denoted as AC) measured at 5 mA/cm2 is significantly increased from 26.8 to 38.7 F/g by the adsorption of RuOx nanoparticles with ultrasonic weltering in 1 MNaOH for 30 min. This method is a promising tool in improving the performance of carbon-based double-layer capacitors. The total specific capacitance of a composite composed of 90 wt.% AC and 10 wt.% RuOx measured at 25 mV/s is about 62.8 F/g, which is increased up to ca. 111.7 F/g when RuOx has been previously annealed in air at 200°C for 2 h. The specific capacitance of RuOx nanoparticles was promoted from 470 to 980 F/g by annealing in air at 200 °C for 2 h. The nanostructure of RuOx was examined from the transmission electron microscopic (TEM) morphology[[department]]化學工程學