Studies on the utilization of forest residues (I) : On the orientation molding of wood particles

[Author abstract]For the perpose of obtaining fundamental information on the profitable utilization of forest residues, experiment on the wood particle molding was carried out. Urea, Melamineurea and phenol resins were synthesized as the binder for particles prepared from forest residues. Two types of particleboards, convensional board and orientation board, were prepared by hot pressing and extrusion molding, and the later was overlaid with lauan veneers (Composite plywood). The effects of orientation of particles on bending properties and dimensional stability of boards or panels were tested in various board density and resin content. From the results of experiments, it was clearfied that composite plywood composed of oriented particleboard core and veneer face has good strength properties and dimensional stability, and could be available in substitution for plywood.[著者抄録]林産廃材からつくられたストランド状パーティクルに,ユリア樹脂,メラミンユリア共縮合樹脂,およびフェノール樹脂を添加してエクストルージョン方式によるボードを成形し,これを芯板とする複合合板の製造研究を行なった。パーティクルの成形には,本研究用に試作した金型を用い,エクストルージョン法ボードと同形態のパーティクル配列の方向性ボードを作成した。比重および含脂率の異なる種々のボードを成形し,成形条件とボード物性の関係を測定した結果,例えば,比重0.6～0.7のユリア製ボード(含脂率8%)は,芯板用単板と類似した異方性を有し,繊維平行向での曲げ強さ380～400 kg/cm^2,線膨張率0.3～0.5%(24hr水中浸漬)を示した。次に上記のパーティクルボードを芯板に用い,その両面に厚さ1mmの単板を繊維を直交させて接着し,3-plyの複合合板を作成し,一般合板との物性比較,および耐候性試験を行なった。合板との物性比較の結果から,試作された複合合板は合板とほぼ同等の曲げ強さを有するが,湿潤時の強度低下が合板よりやや大きいことが認められた。複合合板の耐候性が結合剤によって影響されると思われるので,3種類の結合剤からつくられた種々の複合合板について,乾燥-湿潤の繰返しによる促進劣化試験を行ない,その結果フェノール樹脂製のボードが最も良好な耐候性を有することが明らかにされた