Enhancement of the superconductivity and quantum metallic state in the thin film of superconducting Kagome metal KV$_3$Sb$_5$

Recently V-based Kagome metal attracted intense attention due to the emergence of superconductivity in the low temperature. Here we report the fabrication and physical investigations of the high quality single-crystalline thin films of the Kagome metal KV$_3$Sb$_5$. For the sample with the thickness of about 15 nm, the temperature dependent resistance reveals a Berezinskii-Kosterlitz-Thouless (BKT) type behavior, indicating the presence of two-dimensional superconductivity. Compared with the bulk sample, the onset transition temperature $T^{onset}_{c}$ and the out-of-plane upper critical field $H_{c2}$ are enhanced by 15\% and more than 10 times respectively. Moreover, the zero-resistance state is destroyed by a magnetic field as low as 50 Oe. Meanwhile, the temperature-independent resistance is observed in a wide field region, which is the hallmark of quantum metallic state. Our results provide evidences for the existence of unconventional superconductivity in this material.Comment: 5 pages, 4 figure