High-temperature ex-vessel corium spreading. Part 1: Experimental investigations on ceramic and sacrificial concrete substrates.

International audienceOptimizing melt spreading in the aftermath of a core disruptive accident is crucial for achieving sufficient melt cooling to maintain reactor containment integrity. Two $\approx$ 30 kg-scale experiments performed at the VULCANO facility explore the spreading of high-temperature molten corium-concrete mixtures over ceramic and sacrificial concrete substrates. Imaging of the melt front propagation revealed a 7% increase in spreading length and a 30% increase in maximum front velocity during spreading over sacrificial concrete, despite a reduced mass partaking in spreading due to holdup within the crucible. Infrared imaging of the melt indicated surface temperatures around 45 °C lower during spreading on sacrificial concrete, which is anticipated to result in a roughly three-fold increase in melt viscosity. The reduced mass and elevated viscosity during spreading on sacrificial concrete imply an enhanced spreadability on concrete greater than the observed 7% increase in spreading length. This enhanced spreadability on sacrificial concrete could be explained by the apparent gliding motion of the melt, consistent with reduced friction at the melt-substrate interface. Reduced friction at the melt-substrate interface is best explained by a diphasic film of molten concrete and gaseous concrete decomposition products acting as a lubricant between the melt and solid substrate