In this study, life time calculation of aluminum 7075 alloy with cryogenic and natural aging processes was performed by thermal analysis. The aluminum alloy was quenched after solid solution treatment at 480°C and naturally aged for 10-100 days at room temperature (25°C). Other samples were cryogenically treated at -40°C and -80°C for 2 hours after solid solution treatment at 480°C. After the cryogenic treatment, natural aging was done at room temperature for 10-100 days. At the end of each period determined for the samples, the hardness values were measured. It was observed that there was no significant change in hardness values at the end of 10 and 100 days at -80 °C. Thus, it was determined that the natural aging process does not start a...
The effect of cryogenic treatment (CT) on the microstructure, residual stress, and dimensional stabi...
Para esta investigación se evaluó la influencia del tratamiento criogénico por inmersión y reenvejec...
The effect of natural aging on the aging response of the A1-Zn-Mg-Zr alloy AA7020 was studied using ...
In this study, life time calculation of aluminum 7075 alloy with cryogenic and natural aging process...
The aim of this study is to investigate the effects of cryogenic process (CP) on the properties of 2...
The effect of natural aging (NA) on mechanical properties in double aged aluminum alloys, AA7075, wa...
In order to determine storage life for aluminum alloys it is essential to have a good knowledge on t...
The aging response of open-die-forged 7050 aluminum was studied at various temperatures. This is of ...
In the current study, an effect of cryogenic treatment on the ageing of a B4C particulate reinforced...
The aim of this study is to investigate the effects of cryogenic and room temperature pre-deformatio...
The aim of this study is to investigate the effects of cryogenic and room temperature pre-deformatio...
The effect of cryorolling on microstructural evolution and aging characteristics of an Al–4Zn–2Mg al...
The science of altering the room temperature properties of metals by first exposing them to extreme ...
The effects of natural ageing treatment prior to artificial ageing treatment on the microstructures ...
This paper discusses the effect of deep cryogenic treatment (DCT) on the evolution of natural and ar...
The effect of cryogenic treatment (CT) on the microstructure, residual stress, and dimensional stabi...
Para esta investigación se evaluó la influencia del tratamiento criogénico por inmersión y reenvejec...
The effect of natural aging on the aging response of the A1-Zn-Mg-Zr alloy AA7020 was studied using ...
In this study, life time calculation of aluminum 7075 alloy with cryogenic and natural aging process...
The aim of this study is to investigate the effects of cryogenic process (CP) on the properties of 2...
The effect of natural aging (NA) on mechanical properties in double aged aluminum alloys, AA7075, wa...
In order to determine storage life for aluminum alloys it is essential to have a good knowledge on t...
The aging response of open-die-forged 7050 aluminum was studied at various temperatures. This is of ...
In the current study, an effect of cryogenic treatment on the ageing of a B4C particulate reinforced...
The aim of this study is to investigate the effects of cryogenic and room temperature pre-deformatio...
The aim of this study is to investigate the effects of cryogenic and room temperature pre-deformatio...
The effect of cryorolling on microstructural evolution and aging characteristics of an Al–4Zn–2Mg al...
The science of altering the room temperature properties of metals by first exposing them to extreme ...
The effects of natural ageing treatment prior to artificial ageing treatment on the microstructures ...
This paper discusses the effect of deep cryogenic treatment (DCT) on the evolution of natural and ar...
The effect of cryogenic treatment (CT) on the microstructure, residual stress, and dimensional stabi...
Para esta investigación se evaluó la influencia del tratamiento criogénico por inmersión y reenvejec...
The effect of natural aging on the aging response of the A1-Zn-Mg-Zr alloy AA7020 was studied using ...