Reactivity of nanosized iron-vanadium spinels towards oxygen and cation distribution

International audienceBecause of the division state of nanosized iron-vanadium spinels, iron and vanadium ions are oxidized within the spinel structure. Calorimetric and thermogravimetric analyses, such as infrared spectroscopy, show that Fe 2 + B , V 3 + B and Fe 3 + are successively oxidized into Fe 3 + and V 5 + ions below 450 °C. The mixed valency cation-deficient spinels resulting from these oxidations have a vacancy content that increases with x, which may be higher than those found as yet for this type of oxide.L'etat de division des spinelles de fer-vanadium nanometriques V x Fe 3 - x O 4 (0 x 2) permet d'oxyder au sein-meme de la structure spinelle les ions du fer et du vanadium. Les analyses calorimetriques et thermogravimetriques, ainsi que la spectroscopie infrarouge, montrent que les ions Fe 2 + B , V 3 + B et Fe 2 + A sont oxydes successivement en ions Fe 3 + et V 5 + a des temperatures inferieures a 450 °C. Les spinelles lacunaires a valence mixte qui en resultent, ont un taux en lacunes croissant avec x, qui peut etre superieur a ceux determines jusqu'alors pour ce type d'oxydes