Effects of Cr Content and Surface Finishes on Oxidation Behaviors of Austenitic Fe-Cr-Ni Alloys Exposed in Supercritical Water (SCW)

The scope of this work was to characterize the corrosion resistance of candidate austenitic alloys in supercritical water for the use of the fuel cladding material within the Canadian supercritical water-cooled reactor (SCWR) concept. A series of Commercial austenitic stainless steels (SS) and alloys were exposed to supercritical water for different exposure times up to 500 hours. Two surface finishes were applied â a coarse grinding with 120 grit abrasive or polishing with either 1200 grit or 0.05 Âľm alumina suspension. Gravimetric measurements and electron microscopy techniques were used to evaluate the oxidation behaviors of tested alloys. The superior corrosion resistance of alloy 310S was benefited from a critical Cr content of 25 wt.%. The surface finish played a significant role to vary the oxidation behavior of alloys containing slightly less than the critical Cr content. However, Oxide exfoliation was observed on low Cr content alloys.M.A.S