Ti2AlC has been demonstrated as the promising protective layer material for thermal barrier coatings (TBCs) against calcium–magnesium–alumina–silicate (CMAS) attack. In this study, the reliability of Ti2AlC coatings against the CMAS corrosion was explored, and new Ti2AlC/YSZ TBCs more efficiently resistant to CMAS were designed. The fabricated Ti2AlC coatings inevitably contain some impurity phases (TiC and Al2Ti3), the contents of which were minimized by optimizing the spraying distance. Corrosion tests revealed that Ti2AlC/YSZ TBCs yielded higher resistance to the CMAS attack than YSZ TBCs, but with long-term exposure to CMAS, the Ti2AlC protective coating exhibited microstructure degradation due to the presence of the impurity phases, wh...
To improve the hot corrosion resistance of YSZ thermal barrier coatings, a 25 {micro}m and a 2 {micr...
The CMAS associated degradation of 7YSZ TBC layers is one of the serious problems in the aero engine...
The rise in aero-engine operating temperatures due to economic and environmental issues has generate...
Thermal barrier coatings (TBCs) can improve the high-temperature performance of turbine blades, howe...
EB-PVD yttria stabilized zirconia (YSZ) thermal barrier coatings (TBCs) are susceptible to calcia-ma...
Advanced thermal barrier coatings (TBC) are crucial to improved energy efficiency in next generation...
The evolution of CMAS/VA resistant thermal barrier coatings (TBCs) has been the hot topic in the gas...
To improve the hot corrosion resistance of YSZ thermal barrier coatings, a 25 {micro}m and a 2 {micr...
Thermal barrier coatings (TBCs) have been seriously threatened by calcium-magnesium-alumina-silicate...
Thermal barrier coatings (TBCs) are insulating coatings used in gas turbine engines to improve energ...
State of the art thermal barrier coatings (TBC) commonly made of 7-8 wt. % yttria stabilized zirconi...
Thermal barrier coatings (TBCs) are heat resistant and protective layers used in hot section compone...
During last decades, much effort has been made to develop new alternative thermal barrier coating (T...
Facing the demands on efficiency and operational flexibility of gas turbines thermal barrier coating...
Molten calcium–magnesium–aluminum–silicate (CMAS) mineral particles cause significant degradation of...
To improve the hot corrosion resistance of YSZ thermal barrier coatings, a 25 {micro}m and a 2 {micr...
The CMAS associated degradation of 7YSZ TBC layers is one of the serious problems in the aero engine...
The rise in aero-engine operating temperatures due to economic and environmental issues has generate...
Thermal barrier coatings (TBCs) can improve the high-temperature performance of turbine blades, howe...
EB-PVD yttria stabilized zirconia (YSZ) thermal barrier coatings (TBCs) are susceptible to calcia-ma...
Advanced thermal barrier coatings (TBC) are crucial to improved energy efficiency in next generation...
The evolution of CMAS/VA resistant thermal barrier coatings (TBCs) has been the hot topic in the gas...
To improve the hot corrosion resistance of YSZ thermal barrier coatings, a 25 {micro}m and a 2 {micr...
Thermal barrier coatings (TBCs) have been seriously threatened by calcium-magnesium-alumina-silicate...
Thermal barrier coatings (TBCs) are insulating coatings used in gas turbine engines to improve energ...
State of the art thermal barrier coatings (TBC) commonly made of 7-8 wt. % yttria stabilized zirconi...
Thermal barrier coatings (TBCs) are heat resistant and protective layers used in hot section compone...
During last decades, much effort has been made to develop new alternative thermal barrier coating (T...
Facing the demands on efficiency and operational flexibility of gas turbines thermal barrier coating...
Molten calcium–magnesium–aluminum–silicate (CMAS) mineral particles cause significant degradation of...
To improve the hot corrosion resistance of YSZ thermal barrier coatings, a 25 {micro}m and a 2 {micr...
The CMAS associated degradation of 7YSZ TBC layers is one of the serious problems in the aero engine...
The rise in aero-engine operating temperatures due to economic and environmental issues has generate...