Residual stresses in clad pressure vessel steel measured by contour method

Data from contour method cut surfaces of low alloy steel plates clad in stainless steel. Two plates, each measuring 300 mm (length) x 200 mm (width) x 20 mm (thickness), were extracted from the outer cylindrical structure of a nuclear steam generator. The material was forged 18MND5 (French designation equivalent to A 508 Gr.3 Cl. 1). Stainless steel beads were then deposited, by submerged arc strip cladding, on the plates. One plate was clad in a single layer of AISI 309L, the second one was clad with a double layer, 309L followed by 308L. The datasets are in the form of lists of x, y, z coordinates, with one point per line, whitespace delimited in millimetres. Each cut has four files associated to it, two for each cut surface. For each surface, there is an outline file identifying the cut surface periphery and a points file containing the points lying on the surface. Two .mat files have also been uploaded, with the results from the analyses on the single and double layer clad plates. These measurements are part of a broader experimental investigation to better understand the role of residual stresses in underclad cracking. The contour method was used to characterise residual stresses in conjunction with neutron diffraction measurements. The details of the experimental procedure and other information will be found in the paper “Internal stresses in a clad pressure vessel steel during post-weld heat treatment and their relevance to underclad cracking" Cattivelli et al., soon to be published