A Comparative Study of the Mechanical Properties of Selected Dental Composites with a Dual-Curing System with Light-Curing Composites

Abstract: Dual-curing composites have a wide spectrum of use in practice (rebuilding, reconstruction, and luting). The characterization of this type of material and comparative study of selected mechanical properties with light-cured materials were carried out for this paper. In this study, we used six materials with a dual-cure system—Bulk EZ, Fill-Up!, StarFill 2B, Rebilda DC, MultiCore Flow, Activa Bioactive-Restorative—and three light-cured materials—Filtek Bulk Fill Posterior, Charisma Classic, and G-aenial Universal Flo. The materials were conditioned for 24 h in water at 37 °C before testing. Selected material properties were determined: three-point bending flexural strength, diametral tensile strength, hardness, microhardness, and shrinkage stress. The highest three-point bending flexural strength (TPB) was 137.0 MPa (G-aenial Universal Flo), while the lowest amounted to 86.5 MPa (Activa Bioactive). The diametral tensile strength (DTS) values were in a range from 39.2 MPa (Rebilda DC) to 54.1 MPa (Charisma Classic). The lowest hardness (HV) value of 26 was obtained by the Activa Bioactive material, while the highest values were recorded for Filtek Bulk Fill Posterior and Charisma Classic-53 . The shrinkage stress of the tested materials ranged from 6.3 MPa (Charisma Classic) to 13.2 MPa (G-aenial Universal Flo). Dual-curing composites were found to have similar properties to light-cured composites