Correlation between the emulsion oligomerization parameters for C9 fraction and the characteristics of hydrocarbon resins

This paper investigates the production of hydrocarbon resins by emulsion oligomerization of the С9 fraction hydrocarbons in liquid by-products of oil refining. Such oligomers have a wide range of applications as film-forming agents in paints and anti-color coatings. Emulsion oligomerization was carried out using emulsifiers of the first and second kind. The study was performed at different values of the reaction temperature of the reaction duration, the intensity of agitation; concentrations of the emulsifier; С9:water fraction ratio. The resulting products were estimated according to the following indicators: the yield, unsaturation degree, softening temperature, mean molecular weight, color. Statistical analysis was carried out, the correlation of parameters of emulsion oligomerization and the yield and characteristics of oligomers was established. Given that, it would be possible to establish the optimal conditions for emulsion oligomerization and predict the properties of the products obtained. Specifically, it was established that the yield of hydrocarbon resins does not correlate with the reaction temperature (0.15 and 0.30) and the concentration of emulsifiers (0.08 and 0.03). It was proven that in the intervals studied the variable yield of oligomers depends on the duration of the reaction (correlation 0.88 and 0.81). In the case of oligomerization in the reverse emulsion, a significant correlation with the yield is also demonstrated by agitation intensity (0.51) and a С9:water fraction ratio (0.51). That has made it possible to derive an equation of the yield multiple linear regression dependent on the most significant process parameters. The high values of the yield and bromine number correlation (0.94 and 0.93) give grounds to argue about the progress of oligomerization reaction. The relationship among the characteristics of oligomers has been confirmed. This indicates the possibility of directed adjustment of certain characteristics of hydrocarbon resins