Nanocomposite anion-exchange membranes for redox flow batteries

Introduction: The ion-exchange membrane is a vital part of fuel cells, rechargeable batteries, and other electrochemical devices because it determines their efficiency (1). Anion exchange membranes are currently a hot topic of research because they are more efficient and cost-effective in practical applications (2). Organic–inorganic hybrid membranes found to be excellent materials for practical applications due to their improved electrochemical properties, mechanical strength, chemical and thermal stability. Methods: Layered double hydroxides (LDHs) of Magnesium with Aluminium ([Mg-Al] LDH) were prepared by precipitation at low saturation. 5 wt% PVA solution was prepared. Then a calculated amount of double hydroxide was stirred with PVA solution for 8 hrs and crosslinked using glutaraldehyde. The membranes were characterized by XRD, AC impedance analysis and conducted charge –discharge experiment in redox-flow battery (3). Results & Discussions: Figure 1 shows the XRD pattern of Mg-Al LDHs. The diffraction pattern of the sample is well correlated with the standard diffraction pattern (ICSD PDF# 54-1030). A Galvanostatic charge–discharge experiment was carried out in a redox-flow battery using the prepared membrane as a separator, as shown in (Figure 2). Over multiple cycles, the results showed above 70% efficiency. This indicates a low level of cross mixing of ions (4). Conclusions: We used a co-precipitation method to make nanoparticles of ([Mg-Al] LDH. Its phase purity was revealed by the XRD pattern. The newly fabricated nanocomposite membrane was put to the test as a separator in a redox flow battery. The results of a Galvanostatic charge-discharge test revealed that coulombic efficiency was greater than 70 %. Keywords: Ion-exchange membrane, Redox-flow battery, Charge–discharge experiment, Hybrid membranes References 1. Wang X, Sheng W, Shen Y, Liu L, Dai S, Li N. N-cyclic quaternary ammonium-functionalized anion exchange membrane with improved alkaline stability enabled by aryl-ether free polymer backbones for alkaline fuel cells. J Memb Sci [Internet]. Elsevier B.V.; 2019;587(May):117135. Available from: https://doi.org/10.1016/j.memsci.2019.05.059 2. Yang Q, Li L, Gao XL, Wu HY, Liu FH, Zhang QG, et al. Crown ether bridged anion exchange membranes with robust alkaline durability. J Memb Sci [Internet]. Elsevier B.V.; 2019;578(November 2018):230–8. Available from: https://doi.org/10.1016/j.memsci.2019.02.038 3. Suc M, Yeop H, Young H, Hyun S, Kim T, Oh S, et al. Crosslinked anion exchange membranes with primary diamine-based crosslinkers for vanadium redox fl ow battery application. J Power Sources [Internet]. Elsevier B.V; 2017;363:78–86. Available from: http://dx.doi.org/10.1016/j.jpowsour.2017.07.068 4. Prifti H, Parasuraman A, Winardi S, Lim TM, Skyllas-Kazacos M. Membranes for redox flow battery applications. Membranes (Basel). 2012;2(2):275–306