Activation Volumes Of Carbon Diffusion In Fcc Iron-nickel Alloys

The Dis accommodation technique was used to determine the activation volume of carbon diffusion, ΔV, in six fcc iron-nickel alloys. Measurements were made at temperatures ranging from 68 to 90 °C and pressures up to 6 kbar on samples having a nickel content between 31 and 63 at.%. A maximum activation volume of 3.9 cm3/mole was found at 34 at.% nickel. The compositional dependence of ΔV is satisfactorily reproduced by a magnetic-energy continuum model in which it is assumed that the activation free energy of diffusion is essentially ferromagnetic in origin. © 1972 The American Physical Society