Visualization of impact damage in ceramics using the edge-on impact technique

Projectile impact generates severe fragmentation in ceramics which propagates at high velocities and precedes the penetration of the projectile. The high-speed photographic technique of the Edge-On Impact (EOI) has been developed at the Ernst-Mach-Institute (EMI) in order to visualize dynamic fracture in brittle materials. In a typical EOI test the projectile hits one edge of a specimen and fracture propagation is observed during the first 20 us after impact by means of a Cranz-Schardin highspeed camera. EOI tests allow a characterization of different ceramics by the macroscopic fracture patterns, single crack velocities, and crack front velocities (damage velocities). The phenomenology of damage propagation in several ceramics and a ceramic-metal composite is discussed. The EOI technique is useful for the evaluation of damage models for brittle materials because it enables a direct comparison of model predictions to experimental data obtained during the impact process