The Effect of Injection Moulding Temperature on PET Particles/Fibrils in Blends and MFCs

The microfibrillar composites of polypropylene (PP)/poly(ethylene terephthalate) (PET) have been prepared by twin-screw extrusion, followed by cold drawing. The employed stretch ratio was 4. Further processing was done by injection moulding at three different processing temperatures (210ºC, 230ºC, 280ºC) on PP/PET blends with wt% 70/30 Samples were subjected to extensive characterization in each step of MFC preparing. Fourier Transform Infrared (FTIR) spectroscopy was employed to determine the nature of the interaction between the polymers in the composites.. Thermogravimetric Analysis (TGA) were used to investigate degradation of polymers. The crystallization, melting behaviour and the crystallization morphology were investigated by Dynamic Scanning Calorimetry (DSC) and Polarized Optical Microscopy (POM). Influence of processing temperature on morphology was investigated by using Scanning Electron Microscopy (SEM). The observations from the fracture surfaces were discussed and compared with the mechanical properties, and the results have shown a significant influence of the injection moulding temperature on the morphology development and mechanical properties.The microfibrillar composites of polypropylene (PP)/poly(ethylene terephthalate) (PET) have been prepared by twin-screw extrusion, followed by cold drawing. The employed stretch ratio was 4. Further processing was done by injection moulding at three different processing temperatures (210ºC, 230ºC, 280ºC) on PP/PET blends with wt% 70/30 Samples were subjected to extensive characterization in each step of MFC preparing. Fourier Transform Infrared (FTIR) spectroscopy was employed to determine the nature of the interaction between the polymers in the composites.. Thermogravimetric Analysis (TGA) were used to investigate degradation of polymers. The crystallization, melting behaviour and the crystallization morphology were investigated by Dynamic Scanning Calorimetry (DSC) and Polarized Optical Microscopy (POM). Influence of processing temperature on morphology was investigated by using Scanning Electron Microscopy (SEM). The observations from the fracture surfaces were discussed and compared with the mechanical properties, and the results have shown a significant influence of the injection moulding temperature on the morphology development and mechanical properties.C