Aurivillius phases of PbBi4Ti4O15 doped with Mn3+ synthesized by molten salt technique:Structure, dielectric, and magnetic properties

Doping of manganese (Mn3+/Mn4+) into the Aurivillius phase Pb1-xBi4+xTi4-xMnxO15 was carried out using the molten salt technique for various Mn concentrations (x=0, 0.2, 0.4, 0.6, 0.8, and 1). Single phase samples could be obtained in the composition range with x up to 0.6 as confirmed by X-ray and neutron diffraction analysis. Dielectric measurements show a peak at 801, 803, 813 and 850 K for samples with x=0, 0.2, 0.4, and 0.6, respectively, related to the ferroelectric transition temperature (T-c). The main contribution of the in-plane polarization for x = 0.4 the polarization originates from the dipole moment in the Ti(2)O-6 layer. Mn doping in the Pb1-xBi4+xTi4-xMnxO15 does not show any long range magnetic ordering. (C) 2011 Elsevier Inc. All rights reserved.