Synthesis of ultra-smooth and ultra-low friction DLC based nanocomposite films on rough substrates

Rough TiC/a-C films were intentionally grown on smooth surface to simulate a rough finishing of industrial substrates. Surface roughness and growth dynamics of TiC/a-C nanocomposite films deposited on such rough surfaces by non-reactive pulsed-DC (p-DC) sputtering of graphite targets at 350 kHz pulse frequency were studied using atomic force microscopy, cross-sectional scanning electron microscopy. Intensive concurrent ion impingement during the film growth at higher pulse frequency of p-DC sputtering leads to rapid smoothing of such initial rough surfaces. It was shown that rapid smoothing of initially rough surfaces with RMS roughness similar to 6 nm to