Yttrium-aluminate glasses with high alumina content are potential candidates for various applications ranging from transparent ballistic protections, through infrared transparent windows, to hosts for rare earth elements in materials used for solid state lasers. These glasses are interesting because of their optical and mechanical properties and high chemical and thermal stability. Preparation of bulk Al2O3-Y2O3 glasses is very time and energy consuming and prepared materials are very expensive. Different ways of mentioned bulk glasses preparation were reported, however the combination of flame synthesis and subsequent HP sintering of glass microspheres published by Rosenflanz seems to be very promising from technological and economic point...
The ytterbium aluminum garnet composition YbAG (62.5 mol.% Al2O3, 37.5 mol.% Yb2O3) was prepared in ...
In the Y2O3–Al2O3–B2O3 system, homogeneous glasses were obtained from compositions containing from 5...
The glass formation region in the yttria-alumina-silica system was investigated. Properties of glass...
DSC, SEM-EDS, XRD and high-temperature XRD analysis was used to study thermal and crystallization be...
In this work the yttrium-aluminate glasses with different composition A60Y40M (76.8 mol.% Al2O3), A6...
Binary ytterbium-aluminate glass microspheres with eutectic (79.4 mol. % Al2O3, 20.6 mol. % Yb2O3) c...
Five compositions in the system Al2O3–Y2O3 with high level of homogeneity were prepared in the form ...
The ytterbium aluminum garnet composition YbAG (62.5 mol.% Al2O3, 37.5 mol.% Yb2O3) was prepared in ...
Yttrium aluminate glass microspheres with the eutectic composition 76.8 mol. % Al2O3 and 23.2 mol. %...
International audienceThe glass forming region in the B2O3-Al2O3-Y2O3 composition diagram has been d...
The undoped, and Er-doped yttrium aluminozirconate (AYZ) glasses were prepared by flame synthesis in...
AbstractAluminosilicate glasses containing samarium and yttrium (SmAS and YAS glasses) exhibit high ...
This dissertation is the culmination of the investigation of several aspects of the Y2O3-Al2O3-SiO2 ...
In the work we describe the use of Al2O3–Y2O3 glass microspheres with high alumina contents prepared...
Glass-ceramics are innovative composite materials composed by dispersed crystalline particles within...
The ytterbium aluminum garnet composition YbAG (62.5 mol.% Al2O3, 37.5 mol.% Yb2O3) was prepared in ...
In the Y2O3–Al2O3–B2O3 system, homogeneous glasses were obtained from compositions containing from 5...
The glass formation region in the yttria-alumina-silica system was investigated. Properties of glass...
DSC, SEM-EDS, XRD and high-temperature XRD analysis was used to study thermal and crystallization be...
In this work the yttrium-aluminate glasses with different composition A60Y40M (76.8 mol.% Al2O3), A6...
Binary ytterbium-aluminate glass microspheres with eutectic (79.4 mol. % Al2O3, 20.6 mol. % Yb2O3) c...
Five compositions in the system Al2O3–Y2O3 with high level of homogeneity were prepared in the form ...
The ytterbium aluminum garnet composition YbAG (62.5 mol.% Al2O3, 37.5 mol.% Yb2O3) was prepared in ...
Yttrium aluminate glass microspheres with the eutectic composition 76.8 mol. % Al2O3 and 23.2 mol. %...
International audienceThe glass forming region in the B2O3-Al2O3-Y2O3 composition diagram has been d...
The undoped, and Er-doped yttrium aluminozirconate (AYZ) glasses were prepared by flame synthesis in...
AbstractAluminosilicate glasses containing samarium and yttrium (SmAS and YAS glasses) exhibit high ...
This dissertation is the culmination of the investigation of several aspects of the Y2O3-Al2O3-SiO2 ...
In the work we describe the use of Al2O3–Y2O3 glass microspheres with high alumina contents prepared...
Glass-ceramics are innovative composite materials composed by dispersed crystalline particles within...
The ytterbium aluminum garnet composition YbAG (62.5 mol.% Al2O3, 37.5 mol.% Yb2O3) was prepared in ...
In the Y2O3–Al2O3–B2O3 system, homogeneous glasses were obtained from compositions containing from 5...
The glass formation region in the yttria-alumina-silica system was investigated. Properties of glass...