Fabrication and characterization of PEEK/PEI multilayer composites

Polyetheretherketone (PEEK)/polyetherimide (PEI) blends (50/50, v/v) keeping the crystal phase of PEEK have been manufactured by alternate PEEK/PEI layer stacking. This strategy avoided the complete miscibility of both polymers, keeping layers of PEEK and PEI unmixed along the sample thickness, as well as promoting the formation of a smooth interfacial layer where PEEK and PEI were mixed. The properties of this interface after processing at molten state and different times was studied by DSC, DMA, and X-Ray synchrotron. These techniques allowed monitoring the evolution of glass transition, where isolated Tg’s for both pristine polymers were observed even after long processing time. PEEK crystallinity slightly decreased during manufacturing, whereas PEEK crystal parameters did not vary. These observations show that, although the interface—the zone where both polymers are mixed—grew, layers with pristine polymers remained even after prolonged processing time. The preservation of the PEEK crystallinity was also observed in the mechanical properties of the multilayer PEEK/PEI films, which were compared with pristine PEEK and PEI films. Multilayer samples processed for shorter times rendered higher young modulus, tensile strength, and strain at break.Ángel Alvaredo-Atienza gratefully acknowledges the Community of Madrid for financial support through the framework ‘Sistema Nacional de Garantía Juvenil’ fomented by the European Social Fund and the Youth Employment Initiative. SAXS/WAXS experiments were funded by the Diamond Light Source Synchrotron, (grant number SM20494). This work benefited from the use of the SasView application, originally developed under NSF award DMR-0520547. SasView contains code developed with funding from the European Union’s Horizon 2020 research and innovation programme under the SINE2020 project, grant agreement No 654000