The Impact of Damage in Inconel 718 on Hardness Measured by the Vickers Method

To prevent failure of machine components it is necessary to measure material damage generated in a component throughout its entire lifetime. Damage can be quantified by means of damage parameters. This paper considers the usefulness of hardness measurements to evaluate damage parameter in Inconel 718. Vickers hardness tests were performed on a specimen with a variable cross section area after tensile testing. The specimen’s geometry enabled the evaluation of damage parameter in respect of hardness measurements made on one individual specimen