Kinetic Analysis of Isothermal and Non-Isothermal Reduction of Iron Ore Fines in Hydrogen Atmosphere

Direct reduction of iron ore with H2 has become an alternative technology for iron production that reduces pollutant emissions. The reduction kinetics of iron ore fines in an H2 atmosphere under isothermal and non-isothermal conditions were studied by thermogravimetric analysis. X-ray diffraction and scanning electron microscopy were used to measure the mineral composition and analyse the morphology of the reduced fines, respectively. In the isothermal reduction experiment, it was found that the final reduction time was shorter, the higher the temperature, and the metallic iron particles formed a dense matrix structure. It is likely that the initial stages reduction process is the result of a combination of gaseous diffusion and interfacial chemical reaction mechanisms, and that the later stages a combination of interfacial chemical reaction and solid diffusion is the rate control mechanism. In the non-isothermal experiment, the heating rate had a significant effect on the reaction rate. The results show that the non-isothermal reduction proceeded through three stages: mixing control model, two-dimensional diffusion, and three-dimensional diffusion