Frost Resistance and Mechanism of Circulating Fluidized Bed Fly Ash-Blast Furnace Slag-Red Mud-Clinker Based Cementitious Materials

The motivation of this work is to enhance the long-term frost resistance of circulating fluidized bed fly ash (CFA)-based multisolid waste cementitious material (CSM). In this research, CSM2 is prepared by 30 wt.% CFA, 20 wt.% blast furnace slag (BFS), 10 wt.% red mud (RM), 10 wt.% phosphorus slag (PS), and 30 wt.% cement clinker (CC). The strength and mass of CSM are detected by a press and electronic balance. The hydration products, polymerization degree, thermogravimetric, micromorphology, pore structure, and harmful element leaching are detected by XRD, MAS NMR, TG-DTG, SEM-EDX, MIP, and ICP-MS. The major findings indicate that the strength loss, mass loss, and strength of CSM2 after 25 freeze–thaw cycles (CSM2-25) are 2.35%, 0.36%, and 49.95 MPa, respectively, which is superior to other CSMs and still meets the performance requirements of fly ash Portland cement 42.5#. The main hydration products are C-S-H gel, C/N-A-S-H gel, and ettringite during the freeze–thaw cycle. The polymerization degree and thermogravimetric loss of hydration products in CSM2-25 are 50.65% and 12.82 wt.%, respectively, which are higher than those of other CSMs under the synergy of CFA, BFS, RM, and PS. In addition, the microscopic results show that the interface between the paste and aggregate, micromorphology, and pore structure of CSM2-25 are the densest when the mass ratio of Ca/(Si + Al) is 0.81. These characteristics are beneficial to the improvement of long-term frost resistance in CSM2. Finally, the leaching results of harmful elements in CSM2 after 25 freeze–thaw cycles still meet the WHO standard of drinking water. Therefore, this work provides a reliable reference for the preparation of green cementitious materials with great frost resistance by using CFA, BFS, RM, and PS