DSC analysis of strengthening precipitates in ultrafine Al-Mg-Si alloys

Equal channel angular pressing (ECAP) was carried out on solution annealed samples of Al–Mg–Si–Zr and Al–Mg–Si–Zr–Sc alloys to achieve a substantial grain refinement of the materials. Post ECAP aging was then investigated on the ultrafine grained alloys by DSC and TEM analyses. DSC scans were carried out with heating rates ranging from 5 to 30°C min–1. Peak identification was performed by the support of literature information and TEM analyses. Precipitation kinetics revealed to be similar for both alloys but the Sc-free alloy showed a recrystallization peak at temperatures ranging from 310 to 340°C, depending on the strain accumulated during ECAP. On the contrary, the Sc-containing alloy showed a greater grain stability. Analyses of peak positions and of activation energies as a function of ECAP passes experienced by the samples revealed large modifications of precipitation kinetics in the ultrafine-grained alloys with respect to the coarse-grained materials