Comparative Study of M(Ⅱ)Al (M=Co, Ni) Layered Double Hydroxides for Silicone Foam: Characterization, Flame Retardancy, and Smoke Suppression

To compare the different actions of the two representative transition metal cations of Co2+ and Ni2+ in layered double hydroxides (LDHs), CoAl-LDH and NiAl-LDH intercalated with CO32− were synthesized, and the chemical structures, microstructures, and surface areas thereof were successfully characterized. Then, the two LDHs were utilized as flame retardants and smoke suppressants for silicone foam (SiF). The densities, flame retardancy, smoke suppression, thermal stabilities, and compressive strengths of the two SiF/LDHs nanocomposites were investigated. The introduction of LDHs slightly decreased the density of SiF due to the catalytic actions of Co and Ni during the foaming process of SiF. With respect to the flame retardancy, the addition of only 1 phr of either CoAl-LDH or NiAl-LDH could effectively improve the limiting oxygen index of SiF from 28.7 to 29.6%. Based on the results of vertical flame testing and a cone calorimeter test, the flame retardancy and fire safety of the SiF were effectively enhanced by the incorporation of LDHs. In addition, owing to the good catalytic action and large specific surface area (NiAl-LDH: 174.57 m2 g−1; CoAl-LDH: 51.47 m2 g−1), NiAl-LDH revealed higher efficiencies of flame retardancy and smoke suppression than those of CoAl-LDH. According to the results of energy-dispersive X-ray spectroscopy, Co and Ni participated in the formation of protective char layers, which inhibited the release of SiO2 into the gas phase. Finally, the influences on the thermal decomposition and compressive strength for SiF resulting from the addition of LDHs are discussed