Comparative Study on the Scratch and Wear Resistance of Diamond-like Carbon (DLC) Coatings Deposited on X42Cr13 Steel of Different Surface Conditions

Tribological investigations are of great importance, especially in the case of novel combinations of materials used for the tribosystem. In the current research, multilayer diamond-like carbon coating deposited by plasma enhanced chemical vapour deposition on an X42Cr13 plastic mould tool steel is studied with two different surface conditions of the substrate. On the one hand, it is secondary hardened; on the other hand, it is additively plasma nitrided preceding the diamond-like carbon coating. This latter combined treatment, called duplex treatment, has an increasingly wide range of applications today. However, its effectiveness largely depends on applying the appropriate nitriding technology. The tribological behaviour was characterised by an instrumented scratch test and a reciprocating ball-on-plate wear test. The results demonstrate better scratch resistance for the duplex-treated samples, while they show weaker performance in the applied wear type of loading. The current comparative study reveals the reason for the unexpected behaviour and highlights some critical aspects of the heat treatment procedure. The architecture of the tested multilayer DLC coating is unique, and no tribological results have yet been published on tribosystems combined with an X42Cr13 steel substrate. The presented results may particularly interest tribologists and the materials research community