Mechanical Properties Evolution of the 7B04-T74 Aluminum Alloy in the Marine Atmosphere

The 7xxx-series aluminum alloys are widely used in aircrafts due to their superior performance. The evolution of the mechanical properties of the aluminum alloys caused by marine atmospheric corrosion has become a research hotspot due to the increase in aircraft service time in the marine atmospheric environment. In this work, the evolution of the mechanical properties of the 7B04-T74 aluminum alloy was studied by an alternate immersion test. The surface microstructure was analyzed by SEM, EDS, XRD, and OM. The influence of the marine atmospheric corrosion on mechanical properties was studied by tensile and fatigue tests. The results show that the 7B04-T74 aluminum alloy has good corrosion resistance, as only pitting corrosion occurs in the marine atmospheric environment. The tensile properties of the 7B04-T74 aluminum alloy remained fundamentally the same before and after corrosion. The fatigue properties of the 7B04-T74 aluminum alloy were severely reduced, but the localized pitting corrosion only affected the initiation stage of the crack and had little effect on the crack propagation process