Single crystalline β phase Cu-Zn nanowires: Synthesis and martensitic transformation

Here, we report the synthesis of single crystalline β phase Cu-Zn nanowires (diameter around 150 nm and typical length up to 10 μm) by combining electrodeposition and annealing. The obtained nanowires present temperature driven martensitic transformation similar to that found in bulk samples from B2 to 9R structure. A weak influence of the dimensionality on the martensitic transformation is observed in these nanowires. The possibility to obtain bundles of single crystalline nanowires with tunable martensitic transformation temperature and hysteresis similar to that found in bulk, seems to be a fundamental approach to the development of smart nanosystems based on shape memory alloys.Fil: Haberkorn, Nestor Fabian. Comisión Nacional de Energía Atómica. Gerencia del Area de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche). División Bajas Temperaturas; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; ArgentinaFil: Condó, A. M.. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; ArgentinaFil: Sirena, Martin. Comision Nacional de Energía Atómica. Gerencia de Área Investigaciones y Aplicaciones no Nucleares. Gerencia de Física (Centro Atómico Bariloche). División Resonancias Magnéticas; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; ArgentinaFil: Soldera, Flavio Andres. Universitat Saarland; AlemaniaFil: Lovey, Francisco Carlos. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; Argentin