The influence of Ni and V trace elements on high-temperature tensile properties and aging of A356 aluminium foundry alloy

High-temperature tensile properties of unmodified A356 alloy with and without the addition of Ni or V in traces (600 and 1000 ppm of Ni and V, respectively) were investigated by analyzing samples obtained from sand and permanent mold castings in the as-cast and T6 heat-treated conditions. Tensile tests were performed at 508 K (235 C) at a crosshead speed of 1 mm/min. In addition, samples were subjected to artificial aging at 508 K (235 C) for different times, and corresponding hardness curves were plotted. Microstructures and fracture surfaces, analyzed by FEG-SEM equipped with energy dispersive X-ray spectroscopy, showed that neither Ni nor V addition had a detrimental effect on high-temperature tensile properties. Aging curves showed a strong loss of hardness affecting the T6 class between 30-min and 1-h exposure time. After 6-h aging, no evidence of aging treatment persisted on hardness of the tested material. Hardness values did not reveal any significant difference between the reference alloy and the Ni- and V-containing alloys in both casting conditions, in complete analogy with the tensile properties. Unmodified eutectic silicon particles provided inhomogeneity in the a-Al matrix and acted as the principal source of stress concentration leading to fracture