Energy absorption capability of nanomodified glass/epoxy laminates

The impact response of standard and clay-modified vacuum-infused glass/epoxy laminates was investigated. The activity was oriented to evaluate the enhancements in the energy absorption capability of the laminates due to the nanomodification. Nanomodification was achieved by using Cloisite 30B nanoclays by Southern Clay. Low velocity impact tests were carried out on flat samples of about 4 mm thickness by a drop-weight tower. The results clearly indicate that the nanomodified laminates have a greater capability to absorb the impact energy (with up to 30% increases in dissipated energy) with respect to the standard laminates, also in combination with a decrease of the peak impact force (from 10 to 15%). In some ways, this behaviour can be partly justified by the larger damage exhibited by nanomodified laminates, with projected damage areas more than double the damage areas of standard panels, for the same impact energy