Effects of thin-film accelerated carbonation on steel slag leaching

tThis paper discusses the effects of accelerated carbonation on the leaching behaviour of two types ofstainless steel slags (electric arc furnace and argon oxygen decarburisation slag). The release of majorelements and toxic metals both at the natural pH and at varying pH conditions was addressed. Geo-chemical modelling of the eluates was used to theoretically describe leaching and derive informationabout mineralogical changes induced by carbonation. Among the investigated elements, Ca and Si weremost appreciably affected by carbonation. A very clear effect of carbonation on leaching was observed forsilicate phases; geochemical modelling indicated that the Ca/Si ratio of Ca-controlling minerals shiftedfrom ∼1 for the untreated slag to 0.5–0.67 for the carbonated samples, thus showing that the carbon-ation process left some residual Ca-depleted silicate phases while the extracted Ca precipitated in theform of carbonate minerals. For toxic metals the changes in leaching induced by carbonThis paper discusses the effects of accelerated carbonation on the leaching behaviour of two types of stainless steel slags (electric arc furnace and argon oxygen decarburisation slag). The release of major elements and toxic metals both at the natural pH and at varying pH conditions was addressed. Geochemical modelling of the eluates was used to theoretically describe leaching and derive information about mineralogical changes induced by carbonation. Among the investigated elements, Ca and Si were most appreciably affected by carbonation. A very clear effect of carbonation on leaching was observed for silicate phases; geochemical modelling indicated that the Ca/Si ratio of Ca-controlling minerals shifted from ∼1 for the untreated slag to 0.5–0.67 for the carbonated samples, thus showing that the carbonation process left some residual Ca-depleted silicate phases while the extracted Ca precipitated in the form of carbonate minerals. For toxic metals the changes in leaching induced by carbonation appeared to be mainly related to the resulting pH changes, which were as high as ∼2 orders of magnitude upon carbonation. Depending on the specific shape of the respective solubility curves, the extent of leaching of toxic metals from the slag was differently affected by carbonation