Influence of growth temperature on the pinning landscape of YBa2Cu3O7−δ films grown from Ba-deficient solutions

Cuprate coated conductors are promising materials for the development of large-scale applications, having superior performance over other superconductors. Tailoring their vortex pinning landscape through nanostructure engineering is one of the major challenges to fulfill the specific application requirements. In this work, we have studied the influence of the growth temperature on the generation of intrinsic pinning defects in YBa2Cu3O7-δ films grown by chemical solution deposition using low Ba precursor solutions. We have analysed the critical current density as a function of the temperature, applied magnetic field magnitude and orientation, J c(T,H,θ), to elucidate the nature and strength of pinning sites and correlate the microstructure of the films with their superconducting performance. An efficient pinning landscape consisting of stacking faults and associated nanostrain is naturally induced by simply tuning the growth temperature without the need to add artificial pinning sites. Samples grown at an optimized temperature of 750 °C show very high self-field J c values correlated with an overdoped state and improved J c(T,H,θ) performances.This work has been carried out within the framework of the EUROfusion Consortium and has received funding from the Euratom Research and Training Programme 2014–2018 and 2019–2020 under Grant Agreement No. 633 053. The views and opinions expressed herein do not necessarily reflect those of the European Commission. TEM analysis was funded from the EU Horizon 2020 research and innovation program under grant agreement 823717—ESTEEM3. The authors acknowledge financial support from Spanish Ministry of Economy and Competitiveness through the 'Severo Ochoa' Programme for Centres of Excellence in R&D (SEV-2015-0496 and CEX2019-000917-S), SuMaTe RTI2018-095853-B-C21, co-financed by the European Regional Development Fund), the Catalan Government with Grant 2017-SGR-1519 and the EU COST action NANOCOHYBRI CA16218. We also acknowledge the Scientific Services at ICMAB. J A like to thank the UAB PhD program in Materials Science.With funding from the Spanish government through the ‘Severo Ochoa Centre of Excellence’ accreditation (CEX2019-000917-S).Peer reviewe