Randomized in situ evaluation of surface polishing protocols on the caries-protective effect of resin Infiltrant.

The aim of this placebo-controlled randomized in situ study was to evaluate the effect of different surface polishing protocols on enamel roughness, bacterial adhesion and caries-protective effect of a resin infiltrant. Seventy-five bovine enamel samples having artificial caries lesions were treated with a resinous infiltrant and afterwards randomly dividided into five polishing protocols: aluminum oxide flexible disks (Al2O3-Disks), silicon carbide tips (SIC-Tips), silicon carbide brush (SIC-Brush), silicon carbide polyester strips (SIC-Strips) or no polishing [negative control (NC)]. Average surface roughness (Ra) was assessed by profilometry. Samples were mounted in palatal appliances under a mesh for biofilm accumulation. Fifteen volunteers wore the intraoral appliances (14-days) and cariogenic challenge was triggered by sucrose solutions. Biofilm formed was collected for microbiological analysis of caries-related bacteria (Streptococcus mutans, Lactobacillus acidophilus) and demineralization was assessed by cross-sectional microhardness. Mean Knoop hardness numbers (Kg/mm2) were plotted over lesion depth (µm) and area under the lesion curve was subtracted from sound enamel to determine demineralization (ΔS, Kg/mm2xµm). Data were analyzed by ANOVA and post-hoc comparisons (α = 0.05). NC resulted in significantly higher Ra means than Al2O3-Disks and SIC-Strips. Bacterial counts were not significantly different between the groups (p > 0.05). Regards ΔS means, however none of the groups were significantly different to NC (6983.3 kg/mm2xµm /CI 4246.1-9720.5, p > 0.05). Conclusions: Polishing protocols (Al2O3-Disks, SIC-Strips) significantly decreseased roughness of infiltrated-enamel, however none of the polishing protocols could signicantly decrease bacterial counts nor resulted in significant less demineralization