Pembuatan Material Sandwich Panel Sebagai Pengganti Konstruksi Geladak Kapal Kayu di Wilayah Madura

Sandwich panels are a combination of two wooden plates separated by a core. The benefits of using this specimen are still not maximized, only limited to non-structural use in the manufacture of wooden ships. The purpose of this study was to determine the characteristics of sandwich panel specimens using the casting method and the hand layup method. The results of the density test of the casting method have a better value with a value of 1.11 grams/cm³ while pure wood has a density value of 1.21 grams/cm³. The bending strength results from the hand layup method have a better value with a value of 1299.7 N/mm² while pure wood has a bending strength value of 619.7 N/mm². This study concludes that sandwich panel specimens can replace pure wood.Sandwich panel adalah kombinasi antara dua pelat kayu yang dipisahkan oleh bagian inti (core). Manfaat dari penggunaan spesimen ini masih belum maksimal hanya sebatas penggunaan non struktual pada pembuatan kapal kayu. Tujuan dari penelitian ini adalah untuk mengetahui karakteristik spesimen sandwich panel dengan metode casting dan metode hand layup. Hasil pengujian densitas metode casting memiliki nilai yang lebih baik dengan nilai 1,11 gram/cm³ sedangkan kayu murni memiliki nilai densitas 1,21 gram/cm³. Hasil kekuatan bending dari metode hand layup memiliki nilai yang lebih baik dengan nilai 1299,7 N/mm² sedangkan kayu murni memiliki nilai kekuatan bending 619,7 N/ mm². Penelitian ini menyimpulkan bahwa spesimen sandwich panel dapat menggantikan kayu murni.&nbsp