Add to ORKGLarge inclusions can be the initiation site for fatigue failure in metal components. As melting processes are becoming more refined, the size of the inclusions falls below the level of detectability of the non-destructive testing methods
A processing-microstructure-performance approach is followed to study three bearing steel samples ma...
AbstractThe aim of the present work is to develop a statistical approach for the correlation between...
Funding Information: This research is supported by the State Key Laboratory of Advanced Metallurgy F...
Large inclusions can be the initiation site for fatigue failure in metal components. As melting pro...
The rotating bending fatigue test and the measurement of inclusion size distribution in a material u...
The VHCF behaviour of metallic materials containing microstructural defects such as non-metallic inc...
This doctoral thesis is motivated by the metallurgical problem of non-metallic inclusions, which ari...
The increased demand and requirements for high-strength steels drives the need to better understand ...
3 pages, 3 figures.The Weibull statistic has been widely used to study the inherent scatter existing...
When the quantitative characterization of non-metallic inclusions in steel is done and the effect of...
When the quantitative characterization of non-metallic inclusions in steel is done and the effect of...
The effects of sample area and automated SEM/EDS feature analysis parameters (step size, magnificati...
From an engineering point of view, the fatigue strength variability of cast aluminium alloy componen...
1) To validate the predictions of the Generalised Pareto Distribution (GPD) method for estimating th...
The fatigue property is significantly affected by the inner inclusions in steel. Due to the inhomoge...
A processing-microstructure-performance approach is followed to study three bearing steel samples ma...
AbstractThe aim of the present work is to develop a statistical approach for the correlation between...
Funding Information: This research is supported by the State Key Laboratory of Advanced Metallurgy F...
Large inclusions can be the initiation site for fatigue failure in metal components. As melting pro...
The rotating bending fatigue test and the measurement of inclusion size distribution in a material u...
The VHCF behaviour of metallic materials containing microstructural defects such as non-metallic inc...
This doctoral thesis is motivated by the metallurgical problem of non-metallic inclusions, which ari...
The increased demand and requirements for high-strength steels drives the need to better understand ...
3 pages, 3 figures.The Weibull statistic has been widely used to study the inherent scatter existing...
When the quantitative characterization of non-metallic inclusions in steel is done and the effect of...
When the quantitative characterization of non-metallic inclusions in steel is done and the effect of...
The effects of sample area and automated SEM/EDS feature analysis parameters (step size, magnificati...
From an engineering point of view, the fatigue strength variability of cast aluminium alloy componen...
1) To validate the predictions of the Generalised Pareto Distribution (GPD) method for estimating th...
The fatigue property is significantly affected by the inner inclusions in steel. Due to the inhomoge...
A processing-microstructure-performance approach is followed to study three bearing steel samples ma...
AbstractThe aim of the present work is to develop a statistical approach for the correlation between...
Funding Information: This research is supported by the State Key Laboratory of Advanced Metallurgy F...