Propiedades mecánicas y tribológicas de películas lubricantes de ws2 depositadas por medio de magnetrón sputtering dc no reactivo

wS2 thin films were deposited by using magnetron sputtering on 304 stainless steel substrates to observe material capabilities as a solid lubricant exposed to environments with relative humidity above 40%. Coatings obtained presented hexagonal crystalline structure with combined texture in the (100) and (101) planes, parallel to the c axis and linked to columnar detachment and the formation of a transference film. High ductility was observed from the hardness, elastic moduli, plasticity index, and critical load. Friction coefficients measured by ball-on-disc test with alumina balls showed data around 0.09. Increasing the load from 1 to 10 N improved coating friction behavior. Results show that tribo-oxidation phenomena promotes a transition of the wear mechanisms from adhesive to abrasive.Se depositaron recubrimientos de WS2 por medio de magnetrón sputtering, sobre sustratos de acero inoxidable 304, con el fin de determinar las capacidades del material como lubricante sólido en ambientes con humedades relativas superiores a 40%. Se determinó que los recubrimientos obtenidos poseen estruc-tura hexagonal con textura combinada en planos (100) y (101), los cuales son paralelos al eje c y están relacionados con rompimiento columnar y posterior formación de una película de transferencia. Se determinó alta ductilidad a partir de la obtención de la dureza, módulo de elasticidad, índice de plasticidad y carga crítica. Con la técnica de bola en disco se determinó que al aumentar la carga de 1 a 10 N mejora el comportamiento de la fricción cuando se utiliza un par de alúmina, se encontraron coeficientes de fricción del orden de 0.09, y se observó que la tribo-oxidación posee gran influencia al propiciar la transición de mecanismos de adhesivo a abrasivo