Penentuan Situs Asam Bronsted-Lewis dari ZSM-5 yang Disintesis Menggunakan Silika Amorphous dari Fly Ash Sawit

Fly ash is one of the byproducts of palm oil mill. The silica extracted from fly ash can be utilized for the synthesis of ZSM-5 by hydrothermal methods after  fusion pre-treatment with NaOH. This study aimed to obtain ZSM-5 and determine the characteristic of the synthesized ZSM-5. The synthesis was performed at various composition molar ratio of SiO2/Al2O3 with addition of PEG-400 as template on temperature 100°C during hydrothermal process. The analysis using XRD showed that the two of three synthesized zeolites were ZSM-5 with crystallinity 67.63% and 28.53%. Analysis using FTIR spectroscopy on synthesized ZSM-5 detected many groups including T-OH hydroxyl groups (Si-OH/Al-OH), TO groups (O-Si-O/O-Al-O) and pentasil groups are typical of ZSM-5. From analysis using pyridine adsorption, it can be concluded that the increases ratio of SiO2/Al2O3 causes the number total acid side of the sample increased.Fly ash merupakan salah satu produk sampingan dari pabrik kelapa sawit. Silika yang diekstraksi dari fly ash dapat dimanfaatkan untuk sintesis ZSM-5 dengan metode hidrotermal setelah pra-perlakuan fusi dengan NaOH. Penelitian ini bertujuan untuk mendapatkan ZSM-5 dan mengetahui karakteristik ZSM-5 yang disintesis. Sintesis dilakukan pada berbagai komposisi perbandingan molar SiO2/Al2O3 dengan penambahan PEG-400 sebagai template pada suhu 100 °C selama proses hidrotermal. Analisis menggunakan XRD menunjukkan bahwa dua dari tiga zeolit ​​yang disintesis adalah ZSM-5 dengan kristalinitas 67,63% dan 28,53%. Analisis menggunakan spektroskopi FTIR pada ZSM-5 yang disintesis mendeteksi banyak gugus termasuk gugus hidroksil T-OH (Si-OH/Al-OH), gugus TO (O-Si-O/O-Al-O) dan gugus pentasil yang khas dari ZSM -5. Dari analisis menggunakan adsorpsi piridin, dapat disimpulkan bahwa peningkatan rasio SiO2/Al2O3 menyebabkan jumlah sisi asam total sampel meningkat