Effect of cryogenic treatment on the impact resistance and microstructure of an A 572 steel

En este documento se presentan los resultados de un estudio experimental realizado a unas probetas de acero A 572, con el cual se buscó establecer la influencia de los tratamientos térmicos de temple – criogenia y revenido sobre la resistencia al impacto y la microestructura del material. Se estableció la secuencia de tratamientos de este modo: se trataron 4 probetas a temple a 770ºC, 4 probetas a temple - criogenia a 12 horas de exposición y revenido a 400ºC, 4 probetas a temple – criogenia a 24 horas de exposición y revenido y 4 probetas sin tratamiento. Los resultados indican que la dureza del material tratado criogénicamente a 24 horas aumenta ligeramente con respecto a la probeta tratada criogénicamente a 12 horas y el material sin tratar, sin embargo, no se observó variación de los resultados de energía absorbida por el material con tratamiento criogénico a comparación del material sin tratar, puesto que en la microestructura del material, los granos de martensita revenida se refinan y aparecen precipitados de manganeso, sin embargo, esto no influye en la variación de las propiedades mecánicas del material, exceptuando en la dureza.This paper presents the results of an experimental study carried out on A 572 steel specimens, which sought to establish the influence of the quenching- cryogenics and tempering thermal treatments on the impact resistance and microstructure of the material. The sequence of treatments was established in this way: 4 specimens were treated in a quenching at 770ºC, 4 specimens in a quenching - cryogenics at 12 hours exposure and tempered at 400ºC, 4 specimens at a quenching - cryogenic at 24 hours exposure and tempering and 4 specimens without treatment. The results indicate that the hardness of the cryogenically treated material at 24 hours increases slightly with respect to the cryogenically treated probe at 12 hours and the untreated material, however, no change in the results of energy absorbed by the material with cryogenic treatment was observed compared the untreated material, because the microstructure of the material, in the tempered martensite grains is further refined and manganese precipitate appears, however, it does not influence the variation of the mechanical properties of the material, except in the hardness