Mechanically coherent zeolite 13X/chitosan aerogel beads for effective CO2capture

The constant increase of CO2 concentration in the atmosphere is recognized worldwide to severely impact the environment and human health. Zeolites possess a high adsorption capacity for CO2 removal, but their powdery form prevents their use in many practical applications. When binding agents are used, a partial occlusion of the porosity can severely compromise the adsorption capacity. In this regard, a great challenge is producing compact composite adsorbents while maintaining a high specific surface area to preserve the pristine performance of zeolites. Here, this goal was achieved by preparing beads with a high content of zeolite 13X (up to 90 wt %) using a chitosan aerogel as the binding agent. A facile preparation procedure based on the freeze-drying of hydrogel beads obtained by phase inversion led to a peculiar microstructure in which a very fine polymeric framework firmly embeds the zeolite particles, providing mechanical coherence and strength (compressive strain >40% without bead fragmentation, deformation