Microstructure and Mechanical Properties of Mg–6Al–1Sn–0.3Mn Alloy Sheet Fabricated through Extrusion Combined with Rolling

Hot rolling was carried out in this study to modify the microstructures of an extruded Mg–6Al–1Sn–0.3Mn alloy sheet and investigate its effects on mechanical properties. After hot rolling, the grains and second phase of the extruded alloy sheet were remarkably refined, and the c-axis of a few grains was parallel to the transverse direction. The strength improvement was mainly attributed to the grain and Mg17Al12 particle refinement due to the Hall–Petch effect and the Orowan mechanism. The random orientation of the fine grains resulted in improving ductility and anisotropy