Value Recovery from Waste Liquid Crystal Display Glass Cullet through Leaching: Understanding the Correlation between Indium Leaching Behavior and Cullet Piece Size

For hydrometallurgical recovery of indium from glass cullet after dismantling a waste liquid crystal display (LCD), leaching is the rudimentary stage. Though size reduction of the cullet pieces adds convenience for recycling, from an efficiency and cost-effectiveness perspective regarding leaching process development, determining the proper cullet piece size is essential. Hence, in this study, leaching efficiency of indium as a function of cullet piece size was investigated, wherein the proper mechanical classification of crushed glass cullet could be addressed. The optimum conditions of 5 M mineral acid as the lixiviant, pulp density of 500 g/L, temperature of 75 °C, agitation speed of 500 rpm, 2 h process time were kept constant for the leaching studies. It was concluded that the size of the waste LCD cullet inversely affected the leaching efficiency of indium. For efficient leaching, a smaller cullet size is recommended; hence, waste LCD should be crushed to pieces 1 mm or smaller. Indium leaching behavior comparison using HCl, HNO3, H2SO4 revealed that all three mineral acids had similar leaching efficiencies. The reported process provides the missing link between physical dismantling and chemical processing for indium recovery via techno-economical-sustainable process development