Stress corrosion cracking (SCC) behavior of Ni-free duplex stainless steels containing N and C (Febalance-19Cr-8Mn-0.25C-(0.03, 0.21)N, in wt %) was investigated by using a slow strain rate test (SSRT) in air and aqueous NaCl solution with different tensile directions, including parallel (longitudinal) and perpendicular (transverse) to the rolling direction. It was found that alloying N was effective in increasing the resistance to SCC, while it was higher along the longitudinal direction than the transverse direction. The SCC susceptibility of the two alloys was assessed based on the electrochemical resistance to pitting corrosion, the corrosion morphology, and the fractographic analysis
An investigation has been performed to determine the pitting resistance of stainless steels and stre...
Stress corrosion cracking (SCC) susceptibility of the duplex stainless steels E 1.4162 (U S S32101) ...
Susceptibility to stress corrosion cracking (SCC) of alloy C-22 and Ti Gr-12, two candidate alloys f...
Stress corrosion cracking (SCC) behavior of three duplex stainless steels with a low nickel composit...
The project has been directed towards clarification of the effect of nitrogen alloying on the suscep...
The project has been directed towards clarification of the effect of nitrogen alloying on the suscep...
This article describes the susceptibility of 316L stainless steel to stress corrosion cracking (SCC)...
This article describes the susceptibility of 316L stainless steel to stress corrosion cracking (SCC)...
In comparison to conventional duplex stainless steels (DSS), lean duplex SS are characte...
The stress-corrosion cracking (SCC) behaviour of two lean-duplex stainless steels (DSS 2304 and LDSS...
The stress-corrosion cracking (SCC) behaviour of two lean-duplex stainless steels (DSS 2304 and LDSS...
The effect of bending, rolling, and tensile deformation on stress and strain development in grade 22...
Stress corrosion cracking (SCC) susceptibility of the duplex stainless steels E 1.4162 (U S S32101) ...
AbstractClick Stress Corrosion Cracking (SCC) is an environmentally well-known as a failure caused b...
Understanding the effect of nitrogen content on the crack growth rate (CGR) due to intergranular str...
An investigation has been performed to determine the pitting resistance of stainless steels and stre...
Stress corrosion cracking (SCC) susceptibility of the duplex stainless steels E 1.4162 (U S S32101) ...
Susceptibility to stress corrosion cracking (SCC) of alloy C-22 and Ti Gr-12, two candidate alloys f...
Stress corrosion cracking (SCC) behavior of three duplex stainless steels with a low nickel composit...
The project has been directed towards clarification of the effect of nitrogen alloying on the suscep...
The project has been directed towards clarification of the effect of nitrogen alloying on the suscep...
This article describes the susceptibility of 316L stainless steel to stress corrosion cracking (SCC)...
This article describes the susceptibility of 316L stainless steel to stress corrosion cracking (SCC)...
In comparison to conventional duplex stainless steels (DSS), lean duplex SS are characte...
The stress-corrosion cracking (SCC) behaviour of two lean-duplex stainless steels (DSS 2304 and LDSS...
The stress-corrosion cracking (SCC) behaviour of two lean-duplex stainless steels (DSS 2304 and LDSS...
The effect of bending, rolling, and tensile deformation on stress and strain development in grade 22...
Stress corrosion cracking (SCC) susceptibility of the duplex stainless steels E 1.4162 (U S S32101) ...
AbstractClick Stress Corrosion Cracking (SCC) is an environmentally well-known as a failure caused b...
Understanding the effect of nitrogen content on the crack growth rate (CGR) due to intergranular str...
An investigation has been performed to determine the pitting resistance of stainless steels and stre...
Stress corrosion cracking (SCC) susceptibility of the duplex stainless steels E 1.4162 (U S S32101) ...
Susceptibility to stress corrosion cracking (SCC) of alloy C-22 and Ti Gr-12, two candidate alloys f...