Orientation and Temperature Dependence of Piezoelectric Properties for Sillenite-Type Bi12TiO20 and Bi12SiO20 Single Crystals

The full matrix of electro-elastic constants of sillenite-type crystals Bi12TiO20 (BTO) and Bi12SiO20 (BSO) were determined by the resonance method, with d14 and k14 being on the order of 40–48 pC/N and 31%–36%, respectively. In addition, double-rotated orientation dependence of d33 was investigated, with the maximum values of 25–28 pC/N being achieved in ZXtl45°/54°-cut samples. The electrical resistivity of BSO was found to be two orders higher than that of BTO, being on the order of 7 × 105 Ω cm at 500 °C. The temperature dependence of dielectric and piezoelectric properties were investigated. BSO exhibited a high thermal stability in the temperature range of 25–500 °C, while BTO showed a variation of ~3% in the range of 25–350 °C. The high values of d14 and k14, together with the good thermal stability, make BTO and BSO crystals potential candidates for electromechanical applications in medium temperature range