ANALISIS SIFAT MEKANIK DAN STRUKTUR MIKRO SAMBUNGAN LAS SHIELDING METAL ARC WELDING PADA PLAT MILD STEEL SS400

Shielding Metal Arc Welding (SMAW) is welding process where heat is generate from electric arc between the end ofelectrode and the base metal. Because of the heat from this arc, so the base metal and the end of electrode melt andfreeze together.In this research, used Mild Steel Plate SS400 which is low carbon steel. The material gived weldingtreatment with current variations of 120 A, 130 A and 140 A with Shielding Metal Arc Welding (SMAW) DC+ andelectrode AWS A5.1 E6013 type RD 260 diameter 3.2 mm. Type of connection used single "V" groove with angle 60º,with flat position (1G). Specimens had welded then did tensile test, hardness test, and observation of microstructure.Las Shielding Metal Arc Welding (SMAW) atau sering disebut dengan las elektroda terbungkus adalah prosespengelasan dimana panas dihasilkan dari busur listrik antara ujung elektroda dengan logam yang dilas. Karena panas daribusur ini maka logam induk dan ujung elektroda tersebut mencair dan kemudian membeku bersama. Pada penelitian inimenggunakan Plat Mild Steel SS400 yang merupakan baja karbon rendah. Material diberi perlakuan pengelasan denganvariasi arus 120 A, 130 A dan 140 A dengan menggunakan las Shielding Metal Arc Welding (SMAW) DC+ polaritasterbalik dan elektroda AWS A5.1 E6013 tipe RD 260 diameter 3.2 mm. Jenis kampuh sambungan yang digunakan yaituSingle “V” Groove sudut 60º, dengan posisi pengelasan datar (Flat Position / 1G). Spesimen yang sudah di las kemudiandilanjutkan dengan pengujian tarik, uji kekerasan Rockwell, dan pengamatan struktur mikro