Pengaruh Perlakuan Panas Pada Clad Bend Pipe (API5L) dengan Pengelasan GTAW Overlay Menggunakan UNS N06625 Terhadap Kekuatan Tarik Material

Heat Treatment is a process of heating a material (metal) with a certain temperature and then cooling it using certain media (for example: oil, water, and salt water) with a specified cooling speed. This research used a quenching and tempering heat treatment process on API 5L carbon steel pipe with a diameter of 16 inches (406.4 mm) and a pipe thickness of 1,437 inches (36.5 mm), which previously the carbon steel pipe had an overlay welding process on the inside using UNS N06625 filler metal with protective gas of Argon 99.999% to reduce the corrosion rate along the bending process to become Clad Bend Pipe. The purpose of this study is to find out any effects of heat treatment (Quenching and Tempering) to increase the value of the tensile test results on clad bend pipes.Perlakuan Panas atau biasa disebut dengan Heat Treatment, merupakan suatu proses memanaskan sebuah material (logam) dengan temperatur tertentu dan kemudian didinginkan menggunakan media tertentu (misal: oli, air, dan air garam) dengan kecepatan pendinginan yang ditentukan. Penelitian ini menggunakan proses perlakuan panas quenching dan tempering pada pipa baja karbon API 5L dengan diameter 16 inci (406.4 mm) dan ketebalan pipa 1.437 inci (36.5 mm) yang mana sebelumnya pipa baja karbon tersebutsudah dilakukan proses weld overlaydi bagian dalamnya menggunakan logam pengisi UNS N06625 dengan shielding gas berupa Argon 99.999% untuk mengurangi laju korosi, serta proses bending hingga menjadi Clad Bend Pipe. Tujuan dari penelitian ini adalah untuk mengetahui seberapa berpengaruhnya heat treatment (Quenching dan Tempering) untuk menambah nilai dari hasil uji tarik pada clad bend pipe.