Phase transitions induced by solid-solution: the BCa – BMg substitution in richteritic amphiboles

Eleven compositions along the join Na(NaMg)Mg(5)Si(delta)O(22)(OH)(2)-Na(NaCa)Mg(5)Si(8)O(22)(OH)(2) ("magnesiorichterite"-richterite) have been synthesized at T= 800-850 degrees C and P(H2O) = 0.35-0.5 GPa. The run products have been characterized by electron probe microanalysis (EPMA), synchrotron and conventional X-ray powder diffraction (XRPD), Fourier transformed infrared (FTIR) spectroscopy, and selected area electron diffraction (SAED-TEM). Nominally, the chemical variation along the join call be expressed as (B)Mg(x)(B)Ca(1-x) with 0 C2/m transformation induced by the Ca-Mg chemical Substitution are observed. The phase transition Occurs at B-site composition (X(c)) close to (B)(Na(1)Mg(0.7)Ca(0.3)). C2/m samples with a Ca content of 0.34, 0.45, and 0.54 apfu show, a significant strain tail related to local compositional inhomogeneities. This residual strain disappears Lis the amount of (B)Ca significantly increases with respect to that of (B)Mg. The transformation behavior observed here mirrors that of pyroxenes along the join diopside (CaMgSi(2)O(6))-enstatite (Mg(2)Si(2)O(6))- The Cell parameters of amphiboies with (C)Mg(5), (T)Si(8), and (W)(OH)(2) and variable A- and B-site populations follow almost linear and continuous trends, indicative of small amounts of spontaneous strain accompanying these monoclinic phase transitions and the absence of significant miscibility gaps among different amphibole groups when quenched from higher temperatures of crystallization