The influence of temperature on the cracking of plastic concrete

High early age concrete temperatures can lead to many problems such as an increased rate of cement hydration, as well as an increased rate of moisture loss from fresh concrete which can ultimately lead to the occurrence of plastic shrinkage cracking. Concrete is also batched and cast at various ambient temperatures which greatly influences the temperature development of the concrete after placement. There is a need to understand the influence of concrete temperature on the plastic cracking of concrete. This study investigated the temperature development over the thickness of a concrete slab when exposed to different initial concrete and ambient temperatures as well as the effect these factors have on plastic shrinkage cracking. This was achieved by experiments on concrete samples at varying temperatures while measuring the concrete temperature, pore water evaporation, shrinkage, settlement, setting times and plastic shrinkage cracking magnitude. These tests were conducted in a climate controlled chamber. It was concluded that exposure to higher initial concrete and ambient temperatures significantly increases the average temperature over the thickness of the concrete. The evaporation of pore water was higher when exposed to higher evaporation conditions. The plastic shrinkage, settlement and plastic shrinkage cracking were more severe in the presence of higher initial concrete and ambient temperatures even though the critical period and setting times were reduced due to an increase in the concrete temperature. Finally, the surface temperature of the concrete as tested in slabs up to 100 mm in thickness can be used as a good indication of the temperature development in the lower layers of the concrete