Degree of conversion of Filtek Silorane Adhesive System and Clearfil SE Bond within the hybrid and adhesive layer: An in situ Raman analysis

To examine the degree of conversion (DC) of the adhesive interfaces created by Filtek Silorane Adhesive and Clearfil SE Bond using micro-Raman spectroscopy. METHODS: The adhesives were applied on human dentin in accordance with manufacturer's instructions. Specimens were cut to expose the bonded interfaces to the micro-Raman beam (Ranishaw InVia; laser wl 785 nm). Raman spectra were collected along the dentin/self-etching primer/adhesive interface at 1 microm intervals. The relative intensities of bands associated with mineral (P-O functional group at 960 cm(-1)) and adhesive (C-C-O group at 605 cm(-1)) components within the bonded interface were used to detect monomer penetration into the dentin matrix and to calculate the degree of conversion (C=C at 1640 cm(-1) as reaction peak, C-C-O at 605 cm(-1) as reference peak). Data were statistically analyzed with two-way ANOVA. RESULTS: DC of Filtek Silorane Adhesive was 69+/-7% in the adhesive layer, increasing (p<0.05) to 93+/-5% in the primer and 92+/-9% in the hybrid layer. Clearfil SE Bond showed a DC of 83+/-3% in the hybrid and 85+/-3% in the adhesive layer. Thus, Filtek Silorane Adhesive showed a higher DC than Clearfil SE Bond in the hybrid layer (p<0.05), but a lower DC in the adhesive (p