Femtosecond laser direct writing in SiO 2 ‐Al 2 O 3 binary glasses and thermal stability of Type II permanent modifications

International audienceWe investigate the potential of fabricating thermally stable refractive index contrasts using femtosecond (fs) near-infrared (IR) radiation in aluminosilicate glasses. A set of pure SiO 2-Al 2 O 3 glasses are manufactured, characterized (density and Raman), and investigated after being irradiated by fs laser within the Type II regime. The formation of nanogratings is identified and studied using quantitative birefringence measurements. Their thermal stability is then investigated through 30 minutes step isochronal annealing (up to 1250°C). For both SiO 2 and 50SiO 2-50Al 2 O 3 compositions, the normalized birefringence does not decrease when tested up to 1100°C, while for the 4,6 mol% GeO 2-SiO 2 erased for 20% at 1000°C